Room temperature curing epoxy resin type flame-retardant...

Orgin:epoxy-cn.com | Write:Admin | View: | AddDate:2010-6-18
Purchase, please contact Mr. Wang: 13771380144

Room temperature curing epoxy resin type flame-retardant flame-retardant plastic 9000A-1/113B-----, black for the potting of electronic modules;

 

One, Introduction: 
Department of HL-9000A-1/113B room temperature curing epoxy resin potting material, with a simple operation, excellent gloss after curing, the characteristics of excellent electrical characteristics. Applied to capacitor, electronic ignition, sensors, buzzers and other small and medium-sized electronic components required by the relatively high insulation package. 
 

Two, conventional performance:

Test items

Testing methods or conditions

HL-9000A-1

113B

Appearance

Visual

Black viscous liquid

Dark brown liquid

Density

25℃ g/cm3

1.7~1.8

1.08~1.15

Viscosity

40℃ mpa·s

2000~4000

20~40

Storage period

Room ventilation

Six months

One Year

Three, the use of technology:

Item

Unit or the conditions of 
 

HL-9000A-1/113B

Mixing ratio 
 

Weight ratio 
 

100:25

Can use the time 
 

25℃,min

40

Curing conditions 
 

℃/hrs

25/24 or 60/3

Four, after the curing characteristics:

Item

Unit or the conditions of 
 

HL-9000A-1/113B

Hardness

Shore-D

>76

Dielectric Strength

25℃,kV/mm

>18

Permittivity

25℃,1MHZ

4.1±0.1

Dielectric Loss Tangent 
 

25℃,1MHZ

≤0.01

Volume resistivity 
 

25℃,Ω·cm

2.5×1015

Surface Resistivity 
 

25℃,Ω

1.6×1014

Impact strength 
 

kgf/mm2

>5.8

Flexural strength 
 

kgf/mm2

>17

Compressive strength 
 

kgf/mm2

>30

Flame retardant

UL-94

V-0

Curing shrinkage 
 

%

≤0.5

【Notes】 
● use, be sure to weigh accurately, and fully mixed evenly, so as to ensure uniformity of product quality. 
● This product is mixed at the start of a gradual curing, and its viscosity will gradually rise, and will release some of the heat; 
● mixed with the volume of the plastic the more the faster the reaction, curing speed will be faster and may be accompanied by a large number of heat release, please note that control the amount of time with plastic, because of reaction to speed up because of its use of time will be shortened, try a mixture of the glue used in a short time after; 
● use of time: at 25 ℃ are referring to conditions, 100g mixed viscosity of the glue to double time, it is not operational time, absolutely can not use glue; 
● there is a very small number of people will have prolonged exposure to mild liquid skin allergies, there is mild itch, it is recommended to wear protective gloves when used, please stick to the skin with acetone or alcohol wipe and clean use of cleaning agents; 
● At the use of substantial before a small number of trial skills to master the use of products in order to avoid errors. 
【Storage and packaging 】 
● This product is to be ventilated, cool, dry place sealed preservation, shelf-life of six months, expired qualified by the trial can continue to use; 
Agent-oriented packaging specifications ● 25kg / barrel, curing agent 10kg / barrel.