High temperature epoxy adhesive 9600A/B--Black

Orgin:epoxy-cn.com | Write:Admin | View: | AddDate:2010-6-24
Purchase, please contact Mr. Wang: 13771380144

High temperature epoxy adhesive 9600A/B--Black, high temperature, such as for automotive ignition of potting

 

First, the main component 
A materials: epoxy resin, filler, additive 
B materials: anhydride curing agent, accelerator 
Second, product characteristics: 
1. Best interoperability 
2. Excellent electrical performance 
3. Excellent impact resistance properties of hot and cold 
4. High heat

Ignition coil car ignition coil high-tension line

Third, the main purpose 
Applicable to automotive ignition coil potting 
Fourth, packaging specifications 
A material: 5kg drum 
B materials: 5kg drum 
V. Transportation: 
This product is non-dangerous goods, according to the general goods transportation. 
Sixth, storage: 
1. Confined storage, the best in the next 15 ~ 25 ℃ storage. 
2. Avoid direct sunlight. 
3. Moisture. 
4. Fire. 
5. A shelf life of three months is expected, B is expected for 3 months. 
Seventh, product characteristics

Item

Indicators 
 

Detection based on

Before curing characteristics

Appearance

A

Black viscous liquid

Visual

B

Yellow viscous liquid

Viscosity

(40℃,mPa·s)

A

15000±5000

GB/T2794

B

2000±500

Density

(40℃,g/ml)

A

1.75~1.80

GB/T4472

B

1.30~1.35

Mixing ratio (weight ratio)

A:B=100:70

/

Pot life(40℃,h)

>1

/

Gel time(150℃,min)

180~250

/

After the curing characteristics of
 

Curing material colors

Black

25℃

Hardness (25 ℃, D)

90±5

Shore-D

Flexural strength (25 ℃, N/MM2)

>80

GB/T9341-2000

Surface resistivity (25 ℃, Ω cm)

1015

GB/T1410

Volume resistivity (25 ℃, Ω cm)

1014

GB/T1410

Dielectric constant (25 ℃, 50KHz)

4.0±0.25

GB/T1409

Dielectric loss (25 ℃, 50KHz)

0.60

Water (100 ℃, 1h,%)

<0.15

GB/T1304

Strength of breakdown voltage (25 ℃, KV / mm)

>25

GB/T1048

Thermal conductivity, 25 ℃, W / mK

>0.7

 


 

Eighth, potting process:

 

IX Notes: 
1. Caution 
1) The A group contains fillers were easily layered, mixing before use must be fully uniform, can be 80 ~ 90 ℃ under the conditions of pre-drying in order to stir 6 ~ 8h. 
2) B group of low-temperature storage may have crystal can be 40 ~ 50 ℃ under the conditions of heating to dissolve and then re-use. 
3) by the ratio of accurate measurement of A, B groups were not matched the impact of the prevention of post-curing properties. 
2. Operation Notes 
1) The workplace should be equipped with ventilation equipment and to ensure ventilation. 
2) the operator should wear protective tool operation, avoid direct contact with materials. 
3) If the material accidentally spilled on the skin, use clean cotton cloth, etc., or with warm water after the alkali-free soap to wash, skin irritation or serious burns asked the doctors to help. 
4) Any vapor inhalation when feeling unwell immediately carried Office Outdoor ventilation. 
3. Note Storage 
1) at low temperature, the shade for storage (preferably 15 ~ 25 ℃). 
2) confined to the preservation, in order to avoid entering the water or other impurities. 
3) adhere to FIFO, used in the shelf-life period. 
4) open barrel, it should run out as soon as possible to prevent moisture absorption of impurities into or, if not used after a one-time residue letters should be good.